Durômetros Rockwell total conformidade com DIN EN ISO 6508 e ASTM E-18

Informação de conhecimento Teste de dureza Rockwell (DIN EN ISO 6508)

In 1907, Ludwik published the proposal to use the depth of penetration of a diamond cone to assess the hardness of a material. Furthermore, the influence of the sample surface should be eliminated by applying a preliminary test force. It was not until 1922 that the American Rockwell, building on Ludwik’s idea, succeeded in developing a useful hardness testing method. Because of the simplicity of the method, instruments using the Rockwell hardness test quickly found their way into industrial applications.

Indenter for Rockwell hardness testing

A diamond cone with a point angle of 120° or two hardened steel balls (diameter 1/16 inch = 1.5875 mm or 1/8 inch = 3.175 mm) are used as indenters in the Rockwell test. The steel balls may only be used if this is explicitly required in the product specification or is agreed separately. If required or agreed, carbide balls of 6.356 or 12.70 mm may also be used.

120°
cone de diamante

HRA, HRC, HRD, HR 15 N, 
HR 30 N, HR 45 N

Ø 3.175mm
esfera de aço endurecido

HRE, HRH, HRK

Ø 1.5875mm
esfera de aço endurecido

HRB, HRF, HRG, HR 15 T, HR 30 T, HR 45 T, HR Bm, HR Fm

As 3 etapas do teste de dureza Rockwell

1. The indenter is first pressed into the surface of the specimen with a specific preload F₀. This is to exclude influences of the surface on the hardness value, such as scale layers, hardenings, etc. Under this preload, the indenter initially penetrates the specimen by the distance t₀. To generate the preliminary test force, the specimen is usually pressed against the indenter until the required test force is applied.
    
2. In a second step, the additional test force F₁ is applied. The indenter now penetrates the specimen by a further amount Dt. The additional test force must be applied (starting from the preload) without shock or vibration and without overshooting within a period of 2-8 s and must be kept constant for 4±2s.
    
3. In the third step, the load is relieved again up to the preload F₀. The indenter moves back upwards by the elastic portion of the deformation t_el so that the remaining indentation depth is t_bl. The hardness value is either displayed directly on the hardness tester or can be calculated from the measured indentation depth.

t₀ = indentation depth through test preload F₀
Δt = additional indentation depth through additional test force F₁
t_el = elastic back deformation by relief to the test preload F₀
t_bl = permanent indentation depth after relief to the test preload F₀

Resultados de um teste de dureza Rockwell

O resultado de um teste de dureza Rockwell é determinado da seguinte forma:

In the HRC method, Z is 100 and the scale division Skt is 0.002 mm. If a permanent indentation depth of 0.12 mm is measured, the Rockwell C hardness is 40 HRC.

De acordo com a DIN EN ISO 6508-1, o resultado de um teste de dureza Rockwell é descrito como segue:

60 HRC W   ⇒   Valor de dureza Rockwell

60 HRC W   ⇒   Marcador genérico para "Dureza Rockwell"

60 HRC W   ⇒   Etiqueta para a escala de dureza

60 HRC W   ⇒   Etiqueta para o material do indentador no caso de uma esfera ser usada (não mostrado para o cone de diamante)